| 比重 | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| 密度 | 1.20 g/cc | 0.0434 lb/in³ | ASTM D 792 |
| | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| 平衡吸湿 | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.30 %@Temperature 23.0 °C | 0.30 %@Temperature 73.4 °F | ISO 62 |
| 悬壁梁缺口冲击强度 | 8.38 J/cm@Temperature -10.0 °C | 15.7 ft-lb/in@Temperature 14.0 °F | ASTM D 256 |
| | 8.87 J/cm@Temperature 23.0 °C | 16.6 ft-lb/in@Temperature 73.4 °F | ASTM D 256 |
| | 22.0 kJ/m²@Temperature -30.0 °C | 10.5 ft-lb/in²@Temperature -22.0 °F | 80*10*3; ISO 180/1A |
| | 67.0 kJ/m²@Temperature 23.0 °C | 31.9 ft-lb/in²@Temperature 73.4 °F | 80*10*3; ISO 180/1A |
| 简支梁缺口冲击强度 | 1.40 J/cm²@Temperature -30.0 °C | 6.66 ft-lb/in²@Temperature -22.0 °F | V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| | 7.90 J/cm²@Temperature 23.0 °C | 37.6 ft-lb/in²@Temperature 73.4 °F | V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 冲击试验 | 116 J | 85.6 ft-lb | Multiaxial Impact; ISO 6603 |
| | 76.0 J@Temperature 23.0 °C | 56.1 ft-lb@Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
PC塑胶原料的吸水率较大，加工前一定要预热干燥，纯PC干燥120℃，改性PC一般用110℃温度干燥4小时以上。干燥时间不能超过10小时。一般可用对空挤出法判断干燥是否足够。再生料的使用比例可达20%。在某些情况下，可100%的使用再生料，实际份量要视制品的品质要求而定。再生料不能同时混合不同的色母粒，否则会严重损坏成品的性质。
PC塑料制品由于成本及其它方面的原因，多用改性材料，特别是电工产品，还须增加防火性能，在阻燃的PC和其它塑料合金产品成型时，对注塑机塑化系统的要求是混合好、耐腐蚀，常规的塑化螺杆难以做到，在选购时，一定要预先说明。
PC是一种非晶体工程材料，具有特别好的抗冲击强度、热稳定性、光泽度、抑制细菌特性、阻燃特性以及抗污染性。PC的缺口伊估德冲击强度（otched Izod impact stregth）非常高，并且收缩率很低，一般为0.1%~0.2%。