| TYPICAL PROPERTIES(1) |
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, brk, Type I, 5 mm/min | 640 | kgf/cm² | ASTM D 638 | |
| Tensile Strain, break | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 44300 | kgf/cm² | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 1180 | kgf/cm² | ASTM D 790 | |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 1090 | kgf/cm² | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 39100 | kgf/cm² | ASTM D 790 | |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 36500 | kgf/cm² | ASTM D 790 | |
| Hardness, Rockwell L | 104 | - | ASTM D 785 | |
| Tensile Stress, break | 64 | MPa | ISO 527 | |
| Tensile Strain, break | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 4400 | MPa | ISO 527 | |
| Flexural Stress | 122 | MPa | ISO 178 | |
| Flexural Modulus | 4160 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, unnotched, 23°C | 45 | cm-kgf/cm | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 12 | cm-kgf/cm | ASTM D 256 | |
| Izod Impact, notched, -30°C | 10 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 221 | cm-kgf | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 27 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 25 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 9 | kJ/m² | ISO 180/1A | |
| Charpy Impact, notched, 23°C | 11 | kJ/m² | ISO 179/2C | |
| Charpy Impact, notched, -30°C | 9 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 34 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 33 | kJ/m² | ISO 179/1eU | |
| THERMAL | Value | Unit | Standard | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 131 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 122 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 125 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 5.12E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 7.14E-05 | 1/°C | ASTM E 831 | |
| Vicat Softening Temp, Rate B/50 | 131 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 134 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 132 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 124 | °C | ISO 75/Ae | |
| Relative Temp Index, Elec | 90 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 90 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 90 | °C | UL 746B | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.13 | - | ASTM D 792 | |
| Water Absorption, 24 hours | 0.06 | % | ASTM D 570 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.2 - 0.5 | % | SABIC Method | |
| Melt Flow Rate, 300°C/5.0 kgf | 16.6 | g/10 min | ASTM D 1238 | |
| Melt Volume Rate, MVR at 300°C/5.0 kg | 16 | cm³/10 min | ISO 1133 | |
| ELECTRICAL | Value | Unit | Standard | |
| Relative Permittivity, 1 MHz | 2.9 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.0014 | - | ASTM D 150 | |
| Arc Resistance, Tungsten {PLC} | 7 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 5 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 4 | PLC Code | UL 746A | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94HB Flame Class Rating (3) | 1.47 | mm | UL 94 | |
| UV-light, water exposure/immersion | F1 | - | UL 746C | |