PP(聚丙烯#百折胶|软胶)/GP2300/LG化学
原料描述部分
原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 比重 | | ASTM D-792 | 1.15 | |
| 成型收缩率 | | ASTM D-955 | 0.3-0.5 | % |
| 机械性能 | Izod缺口冲击强度 | | ASTM D-256 | 1.5 | ft.lb/in |
| 拉伸屈服强度 | | ASTM D-638 | 78 | MPa |
| 断裂伸长率 | | ASTM D-638 | 8 | % |
| 弯曲模量 | | ASTM D-790 | 50000 | Kg/cm2 |
| 弯曲模量 | | ASTM 790 | 4900 | MPa |
| Izod缺口冲击强度 | | ASTM D-256 | 8 | Kg.cm/cm |
| 拉伸屈服强度 | | ASTM D-638 | 11400 | psi |
| 弯曲强度 | | ASTM D-790 | 118 | MPa |
| 弯曲模量 | | ASTM D-790 | 710 | psi |
| 拉伸屈服强度 | | ASTM D-638 | 800 | Kg./cm2 |
| 弯曲强度 | | ASTM D-790 | 1200 | Kg/cm2 |
| 弯曲强度 | | ASTM D-790 | 17000 | psi |
| Izod缺口冲击强度 | | ASTM D-256 | 80 | J/m |
| 热性能 | 热变形温度 | 1.82Mpa | ASTM D-648 | 157 | ℃ |
| 耐燃性 | | ASTM D-UL94 | HB | class |
| 热变形温度 | 1.82Mpa | ASTM D-648 | 315 | °F |