| 用途 | | 比重(本色) | 1.19 | g/cm³ | ASTM D792,ISO 1183 | | 熔流率 | | | | | 250°C/10.0 kg | 13 | g/10 min | ASTM D1238 | | 250°C/10.0 kg | 15 | g/10 min | ISO 1133 | | 洛氏硬度(R 计秤) | 122 | | ISO 2039-2 |
| 拉伸模量 | 1900 | MPa | ISO 527-2/50 | | 抗张强度 | | | | | 屈服3 | 62.0 | MPa | ASTM D638 | | 屈服 | 68.0 | MPa | ISO 527-2/50 | | 断裂 | 72.0 | MPa | ISO 527-2/50 | | 伸长率3(屈服) | 100 | % | ASTM D638 | | 弯曲模量 | | | | | --4 | 2100 | MPa | ASTM D790 | | --5 | 2100 | MPa | ISO 178 | | 弯曲强度 | | | | | --4 | 91.0 | MPa | ASTM D790 | | --5 | 90.0 | MPa | ISO 178 | | 简支梁缺口冲击强度6(23°C) | 15 | kJ/m² | ISO 179/1eA | | 悬壁梁缺口冲击强度 | | | | | 23°C, 3.18 mm | 98 | J/m | ASTM D256 | | 23°C, 6.35 mm | 98 | J/m | ASTM D256 | | 23°C6 | 12 | kJ/m² | ISO 180/1A |
| 热变形温度 | | | | | 0.45 MPa, 未退火 | 139 | °C | ISO 75-2/B | | 1.8 MPa, 未退火, 6.40 mm | 130 | °C | ASTM D648 | | 1.8 MPa, 未退火 | 125 | °C | ISO 75-2/A | | 维卡软化温度 | 145 | °C | ISO 306/B50 |
| UL 阻燃等级(0.800 到 3.00 mm) | V-2 | | UL 94 |
| 干燥温度 | | | | | -- | 100 | °C | | | 热风干燥机 | 100 | °C | | | 干燥时间 | | | | | -- | 4.0 | hr | | | 热风干燥机 | 4.0 | hr | | | 建议的最大水分含量 | 1.0 | % | | | 螺筒后部温度 | 260 到 270 | °C | | | 螺筒中部温度 | 270 到 280 | °C | | | 螺筒前部温度 | 280 到 290 | °C | | | 射嘴温度 | 290 | °C | | | 模具温度 | 25.0 到 30.0 | °C | | | 注塑温度 | 6.40 | MPa | | | 背压 | 1.00 | MPa | | | 螺杆转速 | 30 | rpm | |
选择从我们这里购买PC FD-1112的理由: 1. 免费提供样品及小批量试模。 2. 免费提供材质证书及各种认证报告。 3. 24小时技术跟踪支持。 4. PC FD-1112价格更便宜，可为你节省5%以上. 5. 出货周期快，全国范围只需4天。
|