详细说明
CYCOLOY™ C1110HF resin 的重要属性有:
阻燃/额定火焰
高流动性
耐冲击
耐热
柔软
典型应用包括:
电气/电子应用
电气用具
工程/工业配件
户外应用
汽车行业
| 比重 | 1.14 | g/cm³ | ASTM D792 |
| 熔流率 | | | ASTM D1238 |
| 260°C/2.16 kg | 8.0 | g/10 min | |
| 260°C/3.8 kg | 12 | g/10 min | |
| 收缩率 - 流动 (3.20 mm) | 0.50 到 0.70 | % | 内部方法 |
| 室外适用性 | f2 | | UL 746C |
| 拉伸模量3 | 2210 | MPa | ASTM D638 |
| 抗张强度4 (屈服) | 59.3 | MPa | ASTM D638 |
| 伸长率4 | | | ASTM D638 |
| 屈服 | 5.0 | % | |
| 断裂 | 75 | % | |
| 弯曲模量5 (50.0 mm 跨距) | 2380 | MPa | ASTM D790 |
| 弯曲强度5 (屈服, 50.0 mm 跨距) | 86.9 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 | | | ASTM D256 |
| -30°C | 270 | J/m | |
| 23°C | 640 | J/m | |
| 装有测量仪表的落镖冲击 | | | ASTM D3763 |
| -30°C, Energy at Peak Load | 47.5 | J | |
| -30°C, Total Energy | 54.2 | J | |
| 23°C, Energy at Peak Load | 61.0 | J | |
| 23°C, Total Energy | 61.0 | J | |
| 热变形温度 | | | ASTM D648 |
| 0.45 MPa, 未退火, 3.20 mm | 127 | °C | |
| 1.8 MPa, 未退火, 3.20 mm | 110 | °C | |
| 线形膨胀系数 - 流动 (-30 到 30°C) | 0.000072 | cm/cm/°C | ASTM D696 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| 耐电弧性6 | PLC 5 | | ASTM D495 |
| 相比耐漏电起痕指数(CTI) | PLC 3 | | UL 746 |
| 高电弧燃烧指数(HAI) | PLC 0 | | UL 746 |
| 高电压电弧起痕速率 (HVTR) | PLC 1 | | UL 746 |
| 热丝引燃 (HWI) | PLC 3 | | UL 746 |
| UL 阻燃等级 (1.22 mm) | HB | | UL 94 |
| 干燥温度 | 104 到 110 | °C | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 干燥时间，最大 | 8.0 | hr | |
| 建议的最大水分含量 | 0.040 | % | |
| 建议注入量 | 30 到 80 | % | |
| 螺筒后部温度 | 249 到 288 | °C | |
| 螺筒中部温度 | 254 到 293 | °C | |
| 螺筒前部温度 | 260 到 302 | °C | |
| 射嘴温度 | 274 到 302 | °C | |
| 加工（熔体）温度 | 274 到 302 | °C | |
| 模具温度 | 60.0 到 87.8 | °C | |
| 背压 | 0.345 到 0.689 | MPa | |
| 螺杆转速 | 40 到 70 | rpm | |
| 排气孔深度 | 0.038 到 0.076 | mm | |