详细说明
SABIC®PCPC2200Rresin
聚碳酸酯
SABICInnovativePlasticsAsiaPacific
产品说明:
供货地区
亚太地区
添加剂
特性
用途
通用
加工方法
注射成型
| 比重 | 1.20 | g/cm³ | ASTM D792,ISO 1183 |
| 熔流率（熔体流动速率）(300°C/1.2 kg) | 22 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR）(300°C/1.2 kg) | 21.0 | cm³/10min | ISO 1133 |
| 收缩率 - 流动 | | | 内部方法 |
| --3 | 0.50 到 0.70 | % | |
| 3.20 mm | 0.50 到 0.70 | % | |
| 吸水率 | | | |
| 饱和, 23°C | 0.35 | % | ISO 62 |
| 平衡, 23°C | 0.35 | % | ASTM D570 |
| 洛氏硬度 | | | |
| R 级 | 120 | | ASTM D785 |
| R 计秤 | 120 | | ISO 2039-2 |
| 拉伸模量 | | | |
| --4 | 2350 | MPa | ASTM D638 |
| -- | 2350 | MPa | ISO 527-2/1 |
| 抗张强度 | | | |
| 屈服5 | 63.0 | MPa | ASTM D638 |
| 屈服 | 63.0 | MPa | ISO 527-2/50 |
| 伸长率 | | | |
| 屈服5 | 6.0 | % | ASTM D638 |
| 屈服 | 6.0 | % | ISO 527-2/50 |
| 断裂5 | > 70 | % | ASTM D638 |
| 断裂 | > 70 | % | ISO 527-2/50 |
| 弯曲模量 | | | |
| 50.0 mm 跨距6 | 2300 | MPa | ASTM D790 |
| --7 | 2300 | MPa | ISO 178 |
| 弯曲应力 | | | |
| --7,8 | 90.0 | MPa | ISO 178 |
| 屈服, 50.0 mm 跨距6 | 90.0 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 | | | |
| 23°C | 640 | J/m | ASTM D256 |
| -30°C9 | 12 | kJ/m² | ISO 180/1A |
| 23°C9 | 65 | kJ/m² | ISO 180/1A |
| 无缺口悬臂梁冲击 | | | |
| 23°C | 无断裂 | | ASTM D4812,ISO 180/1U |
| -30°C9 | 无断裂 | | ISO 180/1U |
| 装有测量仪表的落镖冲击(23°C, Energy at Peak Load) | 55.0 | J | ASTM D3763 |
| 载荷下热变形温度 | | | |
| 0.45 MPa, 未退火, 3.20 mm | 133 | °C | ASTM D648 |
| 0.45 MPa, 未退火, 64.0 mm 跨距10 | 133 | °C | ISO 75-2/Bf |
| 1.8 MPa, 未退火, 3.20 mm | 122 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距10 | 122 | °C | ISO 75-2/Af |
| 维卡软化温度 | 140 | °C | ISO 306/B50,ASTM D152511 |
| Ball Pressure Test(125°C) | Pass | | IEC 60695-10-2 |
| 线形热膨胀系数 - 流动 | | | |
| -40 到 95°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| 23 到 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| 导热系数 | 0.20 | W/m/K | ASTM C177,ISO 8302 |
| 体积电阻率 | > 1.0E+15 | ohm·cm | ASTM D257,IEC 60093 |
| 介电强度(1.60 mm) | 27 | kV/mm | ASTM D149,IEC 60243-1 |
| 介电常数 | | | ASTM D150,IEC 60250 |
| 60 Hz | 3.00 | | |
| 1 MHz | 3.00 | | |
| 耗散因数 | | | ASTM D150,IEC 60250 |
| 60 Hz | 1.0E-3 | | |
| 1 MHz | 0.010 | | |
| UL 阻燃等级(1.50 mm) | V-2 | | UL 94 |
| 折射率 | 1.586 | | ASTM D542,ISO 489 |
| 透射率(2540 µm) | 88.0 到 90.0 | % | ASTM D1003 |
| 雾度(2540 µm) | | % | ASTM D1003 |
| 干燥温度 | 120 | °C | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 料斗温度 | 60.0 到 80.0 | °C | |
| 料筒后部温度 | 260 到 280 | °C | |
| 料筒中部温度 | 270 到 290 | °C | |
| 料筒前部温度 | 280 到 300 | °C | |
| 射嘴温度 | 270 到 290 | °C | |
| 加工（熔体）温度 | 280 到 300 | °C | |
| 模具温度 | 80.0 到 100 | °C | |