详细说明
LEXAN™121Rresin
聚碳酸酯
SABICInnovativePlasticsAsiaPacific
产品说明:
Nonhalogenated.17.5MFR,forsmall,intricateparts.Internalmoldrelease.
供货地区
亚太地区
添加剂
脱模
特性
无卤
低粘度
可加工性，良好
加工方法
注射成型
| 比重 | | | ASTM D792 |
| -- | 1.20 | g/cm³ | |
| -- | 1.19 | g/cm³ | |
| 特定体积 | 0.835 | cm³/g | ASTM D792 |
| 熔流率（熔体流动速率）(300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| 收缩率 - 流动(3.20 mm) | 0.50 到 0.70 | % | 内部方法 |
| 吸水率 | | | ASTM D570 |
| 24 hr | 0.15 | % | |
| 平衡, 23°C | 0.35 | % | |
| 平衡, 100°C | 0.58 | % | |
| 室外适用性 | f2 | | UL 746C |
| 洛氏硬度 | | | ASTM D785 |
| M 级 | 70 | | |
| R 级 | 118 | | |
| 抗张强度3 | | | ASTM D638 |
| 屈服 | 62.1 | MPa | |
| 断裂 | 68.9 | MPa | |
| 伸长率3 | | | ASTM D638 |
| 屈服 | 7.0 | % | |
| 断裂 | 130 | % | |
| 弯曲模量4(50.0 mm 跨距) | 2340 | MPa | ASTM D790 |
| 弯曲强度4(屈服, 50.0 mm 跨距) | 96.5 | MPa | ASTM D790 |
| 泰伯耐磨性(1000 Cycles, 1000 g, CS-17 转轮) | 10.0 | mg | ASTM D1044 |
| 简支梁缺口冲击强度5 | | | ISO 179/1eA |
| -30°C | 12 | kJ/m² | |
| 23°C | 65 | kJ/m² | |
| 简支梁无缺口冲击强度5 | | | ISO 179/1eU |
| -30°C | 无断裂 | | |
| 23°C | 无断裂 | | |
| 悬壁梁缺口冲击强度 | | | |
| 23°C | 690 | J/m | ASTM D256 |
| -30°C6 | 11 | kJ/m² | ISO 180/1A |
| 23°C6 | 65 | kJ/m² | ISO 180/1A |
| 无缺口悬臂梁冲击 | | | |
| 23°C | 3200 | J/m | ASTM D4812 |
| -30°C6 | 无断裂 | | ISO 180/1U |
| 23°C6 | 无断裂 | | ISO 180/1U |
| 装有测量仪表的落镖冲击(23°C, Energy at Peak Load) | 62.1 | J | ASTM D3763 |
| 落锤冲击(23°C) | 169 | J | ASTM D3029 |
| 拉伸冲击强度7 | 546 | kJ/m² | ASTM D1822 |
| 载荷下热变形温度 | | | ASTM D648 |
| 0.45 MPa, 未退火, 6.40 mm | 138 | °C | |
| 1.8 MPa, 未退火, 6.40 mm | 129 | °C | |
| 维卡软化温度 | 154 | °C | ASTM D15258 |
| 线形热膨胀系数 - 流动(-40 到 95°C) | 6.8E-5 | cm/cm/°C | ASTM E831 |
| 比热 | 1260 | J/kg/°C | ASTM C351 |
| 导热系数 | 0.25 | W/m/K | ASTM C177 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| 体积电阻率 | > 1.0E+17 | ohm·cm | ASTM D257 |
| 介电强度(3.20 mm, in Air) | 15 | kV/mm | ASTM D149 |
| 介电常数 | | | ASTM D150 |
| 50 Hz | 3.17 | | |
| 60 Hz | 3.17 | | |
| 1 MHz | 2.96 | | |
| 耗散因数 | | | ASTM D150 |
| 50 Hz | 9.0E-4 | | |
| 60 Hz | 9.0E-4 | | |
| 1 MHz | 0.010 | | |
| 相比耐漏电起痕指数(CTI) | PLC 2 | | UL 746 |
| 高电弧燃烧指数(HAI) | PLC 1 | | UL 746 |
| 高电压电弧起痕速率 (HVTR) | PLC 2 | | UL 746 |
| 热丝引燃 (HWI) | PLC 2 | | UL 746 |
| UL 阻燃等级(0.711 mm) | HB | | UL 94 |
| Radiant Panel Listing (UL) | YES | | |
| 折射率 | 1.586 | | ASTM D542 |
| 透射率(2540 µm) | 88.0 | % | ASTM D1003 |
| 雾度(2540 µm) | 1.0 | % | ASTM D1003 |
| 干燥温度 | 121 | °C | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 干燥时间，最大 | 48 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 建议注射量 | 40 到 60 | % | |
| 料筒后部温度 | 260 到 282 | °C | |
| 料筒中部温度 | 271 到 293 | °C | |
| 料筒前部温度 | 282 到 304 | °C | |
| 射嘴温度 | 277 到 299 | °C | |
| 加工（熔体）温度 | 282 到 304 | °C | |
| 模具温度 | 71.0 到 93.0 | °C | |
| 背压 | 0.345 到 0.689 | MPa | |
| 螺杆转速 | 40 到 70 | rpm | |
| 排气孔深度 | 0.025 到 0.076 | mm | |