Product Description:
NORYL™ SE100X resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V0 at 6mm and V1 at 1.5mm along with a UL746C Outdoor Suitability rating of F1. NORYL SE100X resin offers strong electrical performance, low moisture absorption, good flow, dimensional stability, and hydrolytic stability. This material is an excellent candidate for indoor and outdoor electrical enclosures, wall plate / socket, and switch / connector applications.
属性
加工方式
资料
视觉搜索
曲线数据
购买地点
单位:SI
| 总览 | |
| 材料状态 | 已商用:当前有效 |
| UL 黄卡1 | E207780-228588 |
| 搜索 UL 黄卡 | SABICNORYL™ Resin |
| 供货地区 | 亚太地区 |
| 用途 | | 电气/电子应用领域电器用具 | 电子显示器建筑应用领域 | 石油/天然气用品照明应用 |
Also Available In | Latin America | North America | |
| 物理性能 | 额定值 | 单位制 | 测试方法 | | 密度 / 比重 | 1.10 | g/cm³ | ASTM D792 | | 收缩率 | | | 内部方法 | | 垂直2 | 0.50 到 0.70 | % | | | 流动 : 3.20 mm | 0.50 到 0.70 | % | | | 室外适用性 | f1 | | UL 746C |
| 机械性能 | 额定值 | 单位制 | 测试方法 | | 抗张强度3 | | | ASTM D638 | | 屈服 | 57.0 | MPa | | | 断裂 | 46.0 | MPa | | | 伸长率3 | | | ASTM D638 | | 屈服 | 6.5 | % | | | 断裂 | 25 | % | | | 弯曲模量4(100 mm 跨距) | 2300 | MPa | ASTM D790 | | 弯曲强度4(屈服, 100 mm 跨距) | 82.0 | MPa | ASTM D790 | | 冲击性能 | 额定值 | 单位制 | 测试方法 | | 悬壁梁缺口冲击强度 | | | ASTM D256 | | -30°C | 90 | J/m | | | 23°C | 260 | J/m | | | 装有测量仪表的落镖冲击 | | | ASTM D3763 | | -30°C, Energy at Peak | 16.0 | J | | | 23°C, Energy at Peak | 40.0 | J | |
| 热性能 | 额定值 | 单位制 | 测试方法 | | 载荷下热变形温度 | | | ASTM D648 | | 0.45 MPa, 未退火, 6.40 mm | 102 | °C | | | 1.8 MPa, 未退火, 6.40 mm | 92.0 | °C | | | RTI Elec5 | 95.0 | °C | UL 746 | | RTI Imp5 | 80.0 | °C | UL 746 | | RTI5 | 95.0 | °C | UL 746 |
| 电气性能 | 额定值 | 单位制 | 测试方法 | | 表面电阻率 | > 1.0E+15 | ohms | ASTM D257 | | 体积电阻率 | 3.1E+16 | ohms·cm | ASTM D257 | | 介电强度(3.20 mm, in Oil) | 18 | kV/mm | ASTM D149 | | 介电常数 | | | ASTM D150 | | 60 Hz | 2.66 | | | | 50 kHz | 2.66 | | | | 1 MHz | 2.57 | | | | 耗散因数 | | | ASTM D150 | | 50 Hz | 6.0E-3 | | | | 60 Hz | 6.0E-3 | | | | 1 MHz | 2.6E-3 | | | | 耐电弧性6 | PLC 7 | | ASTM D495 | | 相比耐漏电起痕指数(CTI) | PLC 1 | | UL 746 | | 高电弧燃烧指数(HAI)(> 1.5 mm) | PLC 0 | | UL 746 | | 高电压电弧起痕速率 (HVTR) | PLC 4 | | UL 746 | | 热丝引燃 (HWI) | | | UL 746 | | > 1.5 mm | PLC 2 | | | | > 6.0 mm | PLC 1 | | | | 可燃性 | 额定值 | 单位制 | 测试方法 | | UL 阻燃等级 | | | UL 94 | | > 1.5 mm | V-1 | | | | > 6.0 mm | V-0 | | | | 极限氧指数 | 33 | % | ASTM D2863 | | Radiant Panel Listing | TRUE | | UL Unspecified |
| 注射 | 额定值 | 单位制 | | | 干燥温度 | 75 到 80 | °C | | | 干燥时间 | 3.0 到 4.0 | hr | | | 建议的最大水分含量 | 0.020 | % | | | 建议注射量 | 30 到 70 | % | | | 料筒后部温度 | 215 到 265 | °C | | | 料筒中部温度 | 225 到 270 | °C | | | 料筒前部温度 | 240 到 275 | °C | | | 射嘴温度 | 250 到 275 | °C | | | 加工（熔体）温度 | 250 到 275 | °C | | | 模具温度 | 55 到 75 | °C | | | 背压 | 0.300 到 0.700 | MPa | | | 螺杆转速 | 20 到 100 | rpm | | | 排气孔深度 | 0.038 到 0.051 | mm | | | 注射说明 | | Injection Molding ParametersDrying Time (Cumulative): 8 hrs |
|