详细说明
XENOY™ 1731 resin
PBT
SABIC Innovative Plastics Asia Pacific
产品说明:
Impact/chemical resistant. UV-Stabilized. Excellent physical property retention in automotive exteriors and OVAD.
| 添加剂 | 紫外线稳定剂 |
| 特性 | 用途 汽车外部零件 加工方法 注射成型 | 比重 | 1.22 | g/cm³ | ASTM D792 | | 特定体积 | 0.820 | cm³/g | ASTM D792 | | 收缩率 | | | 内部方法 | | 流动 : 3.20 mm | 0.50 到 0.70 | % | | | 横向流动 : 3.20 mm | 0.60 到 0.80 | % | |
| 抗张强度 3 (屈服) | 61.4 | MPa | ASTM D638 | | 伸长率 3 (断裂) | 120 | % | ASTM D638 | | 弯曲模量 4 (50.0 mm 跨距) | 2340 | MPa | ASTM D790 | | 弯曲强度 4 (屈服, 50.0 mm 跨距) | 93.1 | MPa | ASTM D790 | | 悬壁梁缺口冲击强度 | | | ASTM D256 | | -30°C | 110 | J/m | | | 23°C | 670 | J/m | | | 23°C, 6.40 mm | 160 | J/m | | | 装有测量仪表的落镖冲击 | | | ASTM D3763 | | -30°C, Total Energy | 61.5 | J | | | 23°C, Total Energy | 61.1 | J | |
| 载荷下热变形温度 | | | ASTM D648 | | 0.45 MPa, 未退火, 6.40 mm | 116 | °C | | | 1.8 MPa, 未退火, 6.40 mm | 107 | °C | | | 线形热膨胀系数 - 流动 (-40 到 95°C) | 8.3E-5 | cm/cm/°C | ASTM E831 | | RTI Elec | 75.0 | °C | UL 746 | | RTI Imp | 75.0 | °C | UL 746 | | RTI | 75.0 | °C | UL 746 |
| 耐电弧性 5 | PLC 5 | | ASTM D495 | | 相比耐漏电起痕指数(CTI) | PLC 2 | | UL 746 | | 高电弧燃烧指数(HAI) | PLC 0 | | UL 746 | | 高电压电弧起痕速率 (HVTR) | PLC 2 | | UL 746 | | 热丝引燃 (HWI) | PLC 2 | | UL 746 | | UL 阻燃等级 (1.50 mm) | HB | | UL 94 |
| 干燥温度 | 110 | °C | | | 干燥时间 | 4.0 到 6.0 | hr | | | 干燥时间，最大 | 8.0 | hr | | | 建议的最大水分含量 | 0.020 | % | | | 建议注射量 | 50 到 80 | % | | | 料筒后部温度 | 243 到 266 | °C | | | 料筒中部温度 | 249 到 271 | °C | | | 料筒前部温度 | 254 到 277 | °C | | | 射嘴温度 | 254 到 271 | °C | | | 加工（熔体）温度 | 260 到 277 | °C | | | 模具温度 | 65.6 到 87.8 | °C | | | 背压 | 0.345 到 0.689 | MPa | | | 螺杆转速 | 50 到 80 | rpm | | | 排气孔深度 | 0.013 到 0.020 | mm | |
|