②原料技术数据| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | | 基本性能 | 吸水率 | 23℃,24小时在水里(2mmt,100℃) | ASTM D-570 | 0.2(2.8) | % | | 物理性能 | 模具收缩率 | 2mmt | ASTM D-955 | 0.3(0.7) | % | | 比重 | --- | ASTM D-792 | 1.75 | --- | | 机械性能 | 拉伸强度 | dry(moist) | ASTM D-638 | 180(150) | MPa | | 拉伸伸长率 | dry(moist) | ASTM D-638 | 3(3) | % | | 弯曲强度 | dry(moist) | ASTM D-790 | 280(240) | MPa | | 弯曲模量 | dry(moist) | ASTM D-790 | 13000(9000) | MPa | | IZOD缺口冲击强度 | dry(moist) | ASTM D-256 | 75(80) | J/M | | 洛氏硬度 | --- | ASTM D-785 | 110 | M scale | | 电气性能 | 体积电阻率 | dry | ASTM D-257 | 1015 | Ω.cm | | 介电常数 | 1016Hz,dry | ASTM D-150 | 4.0 | --- | | 损耗因数 | 1016Hz,dry | ASTM D-150 | 0.011 | --- | | Dielectric breakdown voltage | dry | ASTM D-149 | 22 | KV/mm | | 热 性 能 | 熔点 | --- | --- | 310 | ℃ | | 玻璃转变温度 | --- | --- | 85 | ℃ | | 负荷挠曲温度 | --- | ASTM D-648 | 295 | ℃ | | 线性热膨胀系数 | --- | ASTM D-696 | 2.0(4.5) | ×10-5/℃ | | 阻燃性 | --- | UL 94 | V-0 | --- | | 其它性能 | Glass fiber content | --- | --- | 40 | % |
|
|
|