| TYPICAL PROPERTIES (1) |
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 560 | kgf/cm² | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 510 | kgf/cm² | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 98 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 20500 | kgf/cm² | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 940 | kgf/cm² | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 22700 | kgf/cm² | ASTM D 790 |
| Hardness, Rockwell L | 89 | - | ASTM D 785 |
| Hardness, Rockwell R | 121 | - | ASTM D 785 |
| Tensile Stress, yield, 50 mm/min | 57 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 60 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 120 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2150 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 85 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2250 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 88 | cm-kgf/cm | ASTM D 256 |
| Izod Impact, notched, -30°C | 78 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 714 | cm-kgf | ASTM D 3763 |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C | 70 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 60 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 70 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 65 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 139 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 124 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 6.96E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.47E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C to 80°C, flow | 7.2E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | Passes | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 146 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 140 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 128 | °C | ISO 75/Ae |
| Relative Temp Index, Elec | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 120 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 125 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.18 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.4 - 0.8 | % | SABIC Method |
| Mold Shrinkage, xflow, 3.2 mm (5) | 0.4 - 0.8 | % | SABIC Method |
| Melt Flow Rate, 300°C/1.2 kgf | 10 | g/10 min | ASTM D 1238 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.35 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 9 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | >1.E+15 | Ohm | ASTM D 257 |
| Dielectric Strength, in oil, 0.8 mm | 16.2 | kV/mm | ASTM D 149 |
| Relative Permittivity, 100 Hz | 2.68 | - | ASTM D 150 |
| Relative Permittivity, 1 MHz | 2.64 | - | ASTM D 150 |
| Dissipation Factor, 100 Hz | 0.0012 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.0093 | - | ASTM D 150 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94HB Flame Class Rating (3) | 0.4 | mm | UL 94 |
| Glow Wire Flammability Index 850°C, passes at | 0.8 | mm | IEC 60695-2-12 |
| Glow Wire Flammability Index 960°C, passes at | 1 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature, 1.0 mm | 875 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 3.0 mm | 875 | °C | IEC 60695-2-13 |