| 拉伸应力 (50%应变) | 12.0 | MPa | ISO 527-23 |
| 拉伸应变 (断裂) | > 50 | % | ISO 527-23 |
| 弯曲模量 | | | ASTM D790 |
| -30°C | 1210 | MPa | |
| 23°C | 138 | MPa | |
| 70°C | 62.1 | MPa | |
| 剪切强度 (23°C) | 38.5 | MPa | ASTM D732 |
| 抗泰伯磨耗 (23°C, 1000 Cycles, 1000 g, H-18 转轮) | 50.0 | mg | ASTM D1044 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
| 拉伸应力 | | | ASTM D412 |
| 50%应变, 23°C | 12.4 | MPa | |
| 100%应变, 23°C | 13.8 | MPa | |
| 300%应变, 23°C | 27.6 | MPa | |
| 抗张强度 (断裂, 23°C) | 48.3 | MPa | ASTM D412 |
| 伸长率 (断裂, 23°C) | 500 | % | ASTM D412 |
| 撕裂强度4 (23°C) | 158 | kN/m | ASTM D624 |
| 压缩永久变形 | | | ASTM D395B |
| 23°C, 22.0 hr | 20 | % | |
| 23°C, 22.0 hr5 | 15 | % | |
| 70°C, 22.0 hr | 65 | % | |
| 70°C, 22.0 hr5 | 35 | % | |
| 100°C, 22.0 hr | 75 | % | |
| 100°C, 22.0 hr5 | 50 | % | |
| 巴肖氏弹性 | 40 | % | ASTM D2632 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 装有测量仪表的落镖冲击6 | | | ASTM D3763 |
| -30°C, 2.54 mm, Total Energy7 | 50.0 | J | |
| 23°C, 2.54 mm, Total Energy8 | 57.8 | J | |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 热变形温度 | | | |
| 0.45 MPa, 未退火 | 59.4 | °C | ASTM D648 |
| 0.45 MPa | 59.0 | °C | ISO 75-23 |
| 脆化温度 | < -67.8 | °C | ASTM D746 |
| 玻璃转化温度 | | | |
| -- | -26.1 | °C | DMA |
| --9 | -26 | °C | ISO 11357-23 |
| 维卡软化温度 | | | |
| -- | 168 | °C | ASTM D152510 |
| 50°C/h, B (50N) | 168 | °C | ISO 3063 |
| 线形膨胀系数 - 流动 | 0.00017 | cm/cm/°C | ISO 11359-23 |