color stain for dolomite glaze
| 编号 | 名称 | 成份 | 最高烧成成温度 | 烧成气氛 | 颜色 |
| 氧化 | 还原 |
| sq-528 | 孔雀绿 | cr-al-si-co | 13000c | ★ | ★ | |
| sq-523 | 宝石蓝 | cr-al-co | 13000c | ★ | ★ | |
| sq-521 | 草绿色 | cr-al-zn | 13000c | ★ | ★ | |
| sq-527 | 孔雀兰 | cr-al-co-zn | 13000c | ★ | ★ | |
| sq-525a | 海军兰 | cr-al-co-zn-mg | 13000c | ★ | ★ | |
| sq-020 | 天空兰 | zr-si-v | 13000c | ★ | 0 | |
| sq-104 | 海兰 | zr-si-v-co | 13500c | ★ | ★ | |
| sq-323 | 变色兰 | co-si | 14000c | ★ | ★ | |
| sq-326 | 兰色 | co-al-zn | 14000c | ★ | ★ | |
| sq-048 | 黄色 | zn-pr-si-ce | 13000c | ★ | 0 | |
| sq-049 | 橙色 | se-zr-pr-si-cd-ce | 13000c | ★ | 0 | |
| sq-550 | 粉红色 | ca-si-sn-cr | 13000c | ★ | 0 | |
| sq-006 | 桃红色 | ca-si-sn-cr | 13000c | ★ | 0 | |
| sq-554 | 枣红色 | ca-si-sn-cr | 13000c | ★ | 0 | |
| sq-505 | 紫色 | cr-sn-ce | 13000c | ★ | 0 | |
| sq-064 | 白色 | sn-si-k | 13000c | ★ | ★ | |
| sq-106 | 紫罗兰 | cr-sn-co-si-ca | 13000c | ★ | 0 | |
| sq-100c | 暗橄榄 | zr-si-pr-v-fe-cr | 13000c | ★ | 0 | |
| sq-082 | 兰灰色 | sb-sn | 13000c | ★ | ★ | |
| sq-085 | 烟兰色 | zr-si-co-ni | 13000c | ★ | ★ | |
| sq-072 | 黑色 | fe-cr-mn-zn | 13000c | ★ | ★ | |
| sq-095 | 艳黑 | cr-co-fe-ni | 13000c | ★ | ★ | |
| sq-433 | 镨绿 | zr-pr-v-si | 12500c | ★ | 0 | |
| sq-434 | 橄榄绿 | zr-pr-v-si-cr-zn | 13000c | ★ | 0 | |
| sq-054 | 桔红色 | zr-pr-si-se-cd-s | 12500c | ★ | 0 | |
| sq-193 | 包裹黄 | zr-si-se-cd-s | 13000c | ★ | ★ | |
| sq-195 | 蝦红色 | zr-si-se-cd-s | 13000c | ★ | ★ | |
| sq-196 | 艳红 | zr-si-se-cd-s | 13000c | ★ | ★ | |
| sq-551 | 紫粉红 | ca-sn-si-cr | 13000c | ★ | 0 | |
| sq-341 | 土黄色 | zn-fe-al-cr | 13000c | ★ | 0 | |
| sq-62bs | 棕黄色 | ti-sb-cr | 13000c | ★ | 0 | |
| sq-276 | 棕色 | cr-zn-fe | 13000c | ★ | ★ | |
| sq-476 | 黄棕色 | cr-zn-fe | 13000c | ★ | ★ | |
| sq-476a | 红棕色 | cr-zn-fe-al | 13000c | ★ | ★ | |
| sq-174 | 咖啡色 | cr-zn-fe | 13000c | ★ | 0 | |
| sq-058 | 棕红色 | cr-an-fe | 13000c | ★ | 0 | |
| sq-079 | 黑咖啡 | cr-an-fe | 13000c | ★ | 0 | |
| sq-081 | 灰色 | zr-co-ni | 13000c | ★ | ★ | |
| sq-187 | 黑灰色 | co-ni-si | 13000c | ★ | ★ | |
| sq-352 | 银灰色 | zr-co-si-ni | 13500c | ★ | 0 | |