江苏ABS台湾奇美757价格ABS胶粒757销售ABS塑胶粒757物性ABS原料757生产

　　ABS台湾奇美PA-757物性认证数据表

　　757性能项目757测试条件757测试方法757数值/描述757单位

　　机械性能拉伸强度(引张强度)ASTMD638/ISO527490(6,950)kg/cm²(MPa)[Lb/in2]

　　断裂伸长率ASTMD638/ISO527-%

　　拉伸模量ASTMD638/ISO527-kg/cm²(MPa)[Lb/in2]

　　拉伸屈服伸长率(延伸率)ASTMD638/ISO52720%

　　拉伸断裂伸长率(延伸率)ASTMD638/ISO527-%

　　弯曲强度ASTMD790/ISO178790(11,660)kg/cm²(MPa)[Lb/in2]

　　洛氏硬度ASTMD785R-116

　　IZOD缺口冲击强度1/4"23℃ASTMD256/ISO179-kg·cm/cm(J/M)ft·lb/in

　　1/4"-30℃ASTMD256/ISO17917(3.1)kg·cm/cm(J/M)ft·lb/in

　　1/8"23℃ASTMD256/ISO179-kg·cm/cm(J/M)ft·lb/in

　　1/8"-30℃ASTMD256/ISO17920(3.7)kg·cm/cm(J/M)ft·lb/in

　　Charpy冲击强度23℃（缺口）ASTMD256/ISO179-kg·cm/cm(J/M)ft·lb/in

　　-30℃（无缺口）ASTMD256/ISO179-kg·cm/cm(J/M)ft·lb/in

　　23℃（无缺口）ASTMD256/ISO179-kg·cm/cm(J/M)ft·lb/in

　　-30℃（缺口）ASTMD256/ISO179-kg·cm/cm(J/M)ft·lb/in

　　物性性能比重（密度）ASTMD792/ISO11831.05

　　成型收缩率ASTMD955-%

　　熔融指数（流动系数）200℃/5kgASTMD1238/ISO11331.6g/10min

　　220℃/10kgASTMD1238/ISO113322g/10min

　　吸水率23℃/24HASTMD570/ISO62-%

　　热性能热变形温度退火ASTMD648/ISO7599(210)℃（℉）

　　未退火ASTMD648/ISO7588(190)℃（℉）

　　维卡软化点ASTMD1525/ISOR306105(221)℃（℉）

　　熔点--℃（℉）

　　燃烧性（率）UL941.6mmHB

　　线性膨胀系数ASTMD696/ISO11359-mm/mm.℃

　　加工条件干燥条件80°C下烘料约2~3小时

　　加工温度射嘴180~230°C℃

　　料筒前段190~230℃

　　料筒中段190~230℃

　　料筒后段180~220℃

　　熔体温度-℃

　　模具温度30~70°C℃

　　压力注塑压力-Mpa

　　保压压力-Mpa

　　背压-Mpa

　　螺杆转速-rpm

　　其他备注-

　　颜色-

　　特性高光泽性高刚性。

　　用途电视机前壳/复印机外壳/电话机壳/化妆品盒/轮胎盖