CuZn36、CW507L是一种无铅单相黄铜，具有优异的冷加工性能。它非常适合压印、铆接和压接。Round rods/polygonal rods acc. to EN 12163Temper Diameter Width across flats Tensile strength Rm Yield strength Rp0.2 Elongation % Hardnessmm mm MPa MPa A100 A11.3 A HBfrom to from to min. min. max. min. min. min. min. max.M all all as manufactured – without specified mechanical properties R290 4 80 4 80 290 – 230 – 40 45 – –H070 4 80 4 80 – – – – – – 70 110 R370 4 40 4 35 370 240 – – 12 14 – –H105 4 40 4 35 – – – – – – 105 145 R460 4 10 4 8 460 330 – – 6 8 – –H140 4 10 4 8 – – – – – – 140 –Rectangular rods acc. to EN 12167Temper Thickness Tensile strength Rm Yield strength Rp0.2 Elongation % Hardnessmm MPa MPa A100 A11.3 A HBfrom to min. min. max. min. min. min. min. max.M all as manufactured – without specified mechanical properties R290 3 20 290 – 230 30 40 45 – –H050 3 20 – – – – – – 50 100 R370 3 10 370 240 – 10 12 14 – –H085 3 10 – – – – – – 85 130 R460 3 4 460 330 – 4 6 – – –H105 3 4 – – – – – – 105 145Tubes acc. to EN 12449Temper Wall thickness Tensile strength Rm Yield strength Rp0.2 Elongation % Hardnessmm MPa MPa A100 HV HBmax. min. min. max. min. min. max. min. max.M 20 as manufactured – without specified mechanical properties R290 20 290 – 180 50 – – – –H055 20 – – – – 55 85 50 80 R360 10 360 180 – 25 – – – –H080 10 – – – – 80 115 75 110 R430 5 430 300 – 12 – – – –H110 5 – – – – 110 – 105 –Round wires acc. to EN 12166Temper Diameter Tensile strength Rm Yield strength Rp0.2 Elongation % Hardnessmm MPa MPa A100 A11.3 A HBfrom to min. min. max. min. min. min. min. max.M all as manufactured – without specified mechanical properties R290 0.5 20 290 – 230 30 40 45 – –H055 1.5 20 – – – – – – 55 110 R370 0.5 20 370 240 – 10 12 14 – –H095 1.5 20 – – – – – – 95 140 R460 0.5 5 460 330 – 4 6 – – –H115 1.5 5 – – – – – – 115 155 R550 0.5 4 550 450 – 2 5 – – –H130 1.5 4 – – – – – – 130 170 R700 0.5 4 700 550 – – – – – –H160