| TYPICAL PROPERTIES(1) |
| MECHANICAL/机械性能 | Value/值 | Unit/单位 | Standard/标准 |
| Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 50 mm/min | 58 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I / 抗张程度,断裂,类型I, 50 mm/min | 61 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I / 拉伸伸长,屈服,类型I, 50 mm/min | 6 | % | ASTM D 638 |
| Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 50 mm/min | 130 | % | ASTM D 638 |
| Tensile Modulus / 拉伸模量, 50 mm/min | 2100 | MPa | ASTM D 638 |
| Flexural Stress, yld / 挠曲强度, 屈服 , 1.3 mm/min, 50 mm span | 88 | MPa | ASTM D 790 |
| Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span | 2060 | MPa | ASTM D 790 |
| Tensile Stress, yield / 抗张程度,屈服, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Stress, break / 抗张程度,断裂, 50 mm/min | 60 | MPa | ISO 527 |
| Tensile Strain, yield / 拉伸伸长,屈服, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break / 拉伸伸长,断裂, 50 mm/min | 125 | % | ISO 527 |
| Tensile Modulus / 拉伸模量, 1 mm/min | 2100 | MPa | ISO 527 |
| Flexural Stress, yield / 弯曲强度,屈服, 2 mm/min | 85 | MPa | ISO 178 |
| Flexural Modulus / 挠曲模量, 2 mm/min | 2200 | MPa | ISO 178 |
| Hardness / 硬度, H358/30 | 90 | MPa | ISO 2039-1 |
| IMPACT/冲击性能 | Value/值 | Unit/单位 | Standard/标准 |
| Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C | 801 | J/m | ASTM D 256 |
| Izod Impact, notched / 悬臂梁缺口冲击强度, -30°C | 678 | J/m | ASTM D 256 |
| Izod Impact, notched / 悬臂梁缺口冲击强度, -50°C | 587 | J/m | ASTM D 256 |
| Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C, 6.4mm | 640 | J/m | ASTM D 256 |
| Izod Impact, double-gated, 23°C | 1068 | J/m | SABIC bbbbbb |
| Instrumented IMPACT Total Energy / 装有测量仪表的落镖冲击总能量, 23°C | 52 | J | ASTM D 3763 |
| Izod Impact, unnotched / 无缺口悬臂梁冲击 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, unnotched / 无缺口悬臂梁冲击 80*10*3 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*3 +23°C | 70 | kJ/m2 | ISO 180/1A |
| Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*3 -30°C | 55 | kJ/m2 | ISO 180/1A |
| Izod Impact, notched / 悬臂梁缺口冲击强度 63.5*12.7*3.2, 23°C | 80 | kJ/m2 | ISO 180/4A |
| Izod Impact, notched / 悬臂梁缺口冲击强度 63.5*12.7*3.2, -30°C | 65 | kJ/m2 | ISO 180/4A |
| Charpy（简支梁缺口冲击强度） 23°C, V-notch（V型切口） Edgew 80*10*3 sp=62mm | 75 | kJ/m2 | ISO 179/1eA |
| Charpy（简支梁缺口冲击强度） -30°C, V-notch（V型切口） Edgew 80*10*3 sp=62mm | 60 | kJ/m2 | ISO 179/1eA |
| Charpy（简支梁缺口冲击强度） 23°C, Unnotch（无缺口） Edgew 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy（简支梁缺口冲击强度） -30°C, Unnotch（无缺口） Edgew 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| THERMAL/热性能 | Value/值 | Unit/单位 | Standard/标准 |
| Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50 | 142 | °C | ASTM D 1525 |
| HDT（热变形温度）, 0.45 MPa, 3.2 mm, unannealed （未退火） | 134 | °C | ASTM D 648 |
| HDT（热变形温度）, 1.82 MPa, 3.2mm, unannealed （未退火） | 120 | °C | ASTM D 648 |
| HDT（热变形温度）, 1.82 MPa, 6.4 mm, unannealed （未退火） | 124 | °C | ASTM D 648 |
| CTE（线形膨胀系数）, -40°C to 40°C, flow（流动） | 6.66E-05 | 1/°C | ASTM E 831 |
| CTE（线形膨胀系数）, -40°C to 40°C, xflow（横向） | 6.66E-05 | 1/°C | ASTM E 831 |
| CTE（线形膨胀系数）, 23°C to 80°C, flow（流动） | 7.2E-05 | 1/°C | ISO 11359-2 |
| CTE（线形膨胀系数）, 23°C to 80°C, xflow（横向） | 7.7E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | – | IEC 60695-10-2 |
| Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50 | 140 | °C | ISO 306 |
| Vicat Softening Temp, Rate / 维卡软化温度，等级 B/120 | 142 | °C | ISO 306 |
| HDT（热变形温度）/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 135 | °C | ISO 75/Be |
| HDT（热变形温度）/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 124 | °C | ISO 75/Ae |
| Relative Temp Index, Elec / 相对热指数， 电性能 | 125 | °C | UL 746B |
| Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能 | 115 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能 | 120 | °C | UL 746B |
| PHYSICAL/物理性能 | Value/值 | Unit/单位 | Standard/标准 |
| Specific Gravity / 比重 | 1.18 | – | ASTM D 792 |
| Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm | 0.4 – 0.8 | % | SABIC bbbbbb |
| Mold Shrinkage / 收缩率, xflow（横向）, 3.2 mm | 0.4 – 0.8 | % | SABIC bbbbbb |
| Melt Flow Rate / 熔流率,, 300°C/1.2 kgf | 10 | g/10 min | ASTM D 1238 |
| Density / 密度 | 1.19 | g/cm3 | ISO 1183 |
| Water Absorption / 吸水率, (23°C/sat) | 0.35 | % | ISO 62 |
| Moisture Absorption / 吸水率, 平衡 (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Melt Volume Rate / 溶化体积流率, MVR at 300°C/1.2 kg | 9 | cm3/10 min | ISO 1133 |
| ELECTRICAL/电气性能 | Value/值 | Unit/单位 | Standard/标准 |
| Dielectric Strength, in oil / 耐电强度，在油中, 3.2 mm | 17 | kV/mm | ASTM D 149 |
| Relative Permittivity / 相对介电常数, 50/60 Hz | 2.95 | – | ASTM D 150 |
| Relative Permittivity / 相对介电常数, 1 MHz | 2.9 | – | ASTM D 150 |
| Dissipation Factor / 耗散因素, 50/60 Hz | 0.0024 | – | ASTM D 150 |
| Dissipation Factor / 耗散因素, 1 MHz | 0.0085 | – | ASTM D 150 |
| Hot Wire Ignition / 热丝引燃 {PLC) | 1 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface / 高电流电弧引燃，表面 {PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index / 相比耐漏电起痕指数 (UL) {PLC} | 3 | PLC Code | UL 746A |
| Volume Resistivity / 体积电阻率 | >1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity ROA / 表面电阻率 | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil / 耐电强度，在油中, 3.2 mm | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity / 相对介电常数, 50/60 Hz | 2.6 | – | IEC 60250 |
| Relative Permittivity / 相对介电常数, 1 MHz | 2.7 | – | IEC 60250 |
| Dissipation Factor / 耗散因素, 50/60 Hz | 0.001 | – | IEC 60250 |
| Dissipation Factor / 耗散因素, 1 MHz | 0.0085 | – | IEC 60250 |
| Comparative Tracking Index / 相比耐漏电起痕指数 | 225 | V | IEC 60112 |
| FLAME CHARACTERISTICS/火焰特性 | Value/值 | Unit/单位 | Standard/标准 |
| UL Recognized, 94V-0 Flame Class Rating / 阻燃等级 (3) | 1.49 | mm | UL 94 |
| UL Recognized, 94-5VA Rating (3) | 2.99 | mm | UL 94 |
| Glow Wire Flammability Index / 灼热丝易燃指数 960°C, passes at | 1 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature / 热灯丝点火温度, 1.0 mm | 825 | °C | IEC 60695-2-13 |
| Oxygen Index / 极限氧指数 (LOI) | 35 | % | ISO 4589 |
| UV-light, water exposure/immersion / 紫外线暴露，耐水/浸渍 | F1 | – | UL 746C |