| Physical Properties物理性质 | Metric公制数据 | English英制数据 | Comments测试方法 |
| Density密度 | 1.11g/cc | 0.0401lb/in³ | DAM; ISO 1183 |
| Water Absorption吸水率 | 1.3 %@Temperature 23.0 °C | 1.3 %@Temperature 73.4 °F | Immersion 24h; DAM; ISO 62, Similar to |
| 1.3 %@Thickness 1.00 mm,Temperature 23.0 °C | 1.3 %@Thickness 0.0394 in,Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to |
| Linear Mold Shrinkage线性收缩率 | 0.016cm/cm@Thickness 3.20 mm | 0.016in/in@Thickness 0.126 in | Normal; DAM; ASTM D955 |
| 0.018cm/cm@Thickness 3.20 mm | 0.018in/in@Thickness 0.126 in | Parallel; DAM; ASTM D955 |
| Mechanical Properties力学性能 | Metric公制数据 | English英制数据 | Comments测试方法 |
| Tensile Strength, Yield屈服拉伸强度 | 40.0MPa@Temperature 23.0 °C | 5800psi@Temperature 73.4 °F | 50%RH; ISO 527 |
| 62.0MPa@Temperature 23.0 °C | 8990psi@Temperature 73.4 °F | DAM; ISO 527 |
| Elongation at Break断裂伸长率 | 25 %@Temperature 23.0 °C | 25 %@Temperature 73.4 °F | DAM; nominal; ISO 527 |
| 40 %@Temperature 23.0 °C | 40 %@Temperature 73.4 °F | DAM; ISO 527 |
| >= 50 %@Temperature 23.0 °C | >= 50 %@Temperature 73.4 °F | 50%RH; nominal; ISO 527 |
| Elongation at Yield屈服伸长率 | 5.5 %@Temperature 23.0 °C | 5.5 %@Temperature 73.4 °F | DAM; ISO 527 |
| 15 %@Temperature 23.0 °C | 15 %@Temperature 73.4 °F | 50%RH; ISO 527 |
| Tensile Modulus拉伸模量 | 1.10GPa@Temperature 23.0 °C | 160ksi@Temperature 73.4 °F | 50%RH; ISO 527 |
| 2.40GPa@Temperature 23.0 °C | 348ksi@Temperature 73.4 °F | DAM; ISO 527 |
| Flexural Modulus弯曲弹性模量 | 2.27GPa@Temperature 23.0 °C | 329ksi@Temperature 73.4 °F | DAM; ISO 178 |
| Izod Impact, Notched悬臂梁缺口冲击强度(ISO) | 10.0kJ/m²@Temperature -40.0 °C | 4.76ft-lb/in²@Temperature -40.0 °F | DAM; ISO 180/1A |
| 16.0kJ/m²@Temperature 23.0 °C | 7.61ft-lb/in²@Temperature 73.4 °F | DAM; ISO 180/1A |