| Physical Properties物理性质 | Metric公制数据 | English英制数据 | Comments测试方法 |
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Water Absorption吸水率 | 0.30 %@Temperature 23.0 °C | 0.30 %@Temperature 73.4 °F | Equilibrium 50%RH; ISO 62, Similar to |
| Linear Mold Shrinkage, Flow线性收缩率/流动 | 0.019 cm/cm@Thickness 2.00 mm | 0.019 in/in@Thickness 0.0787 in | Parallel; ISO 294-4 |
| Linear Mold Shrinkage, Transverse线性收缩率/横向 | 0.018 cm/cm@Thickness 2.00 mm | 0.018 in/in@Thickness 0.0787 in | Normal; ISO 294-4 |
| Melt Flow熔体流动速率 | 15 g/10 min@Load 2.16 kg,Temperature 190 °C | 15 g/10 min@Load 4.76 lb,Temperature 374 °F | ISO 1133 |
| Mechanical Properties力学性能 | Metric公制数据 | English英制数据 | Comments测试方法 |
| Hardness, Rockwell R罗氏硬度R | 120 | 120 | ISO 2039/2 |
| Tensile Strength, Yield屈服拉伸强度 | 73.0 MPa@Temperature 23.0 °C | 10600 psi@Temperature 73.4 °F | ISO 527 |
| Elongation at Break断裂伸长率 | 25 %@Temperature 23.0 °C | 25 %@Temperature 73.4 °F | nominal; ISO 527 |
| Elongation at Yield屈服伸长率 | 12 %@Temperature 23.0 °C | 12 %@Temperature 73.4 °F | ISO 527 |
| Tensile Modulus拉伸模量 | 3.20 GPa@Temperature 23.0 °C | 464 ksi@Temperature 73.4 °F | ISO 527 |
| Charpy Impact, Notched | 0.800 J/cm²@Temperature 23.0 °C | 3.81 ft-lb/in²@Temperature 73.4 °F | ISO 179/1eA |
| Electrical Properties电性能 | Metric公制数据 | English英制数据 | Comments测试方法 |
| Comparative Tracking Index | 600 V@Thickness 3.00 mm,Temperature 23.0 °C | 600 V@Thickness 0.118 in,Temperature 73.4 °F | UL 746A |
| Thermal Properties热性能 | Metric公制数据 | English英制数据 | Comments测试方法 |
| Deflection Temperature at热变形温度 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75-1/-2 |
| UL RTI, Electrical相对温度指数 | 50.0 °C@Thickness 0.800 mm | 122 °F@Thickness 0.0315 in | UL 746B |
| 110 °C@Thickness 1.50 mm | 230 °F@Thickness 0.0591 in | UL 746B |
| 110 °C@Thickness 3.00 mm | 230 °F@Thickness 0.118 in | UL 746B |
| UL RTI, Mechanical with Impact机械冲击热指数 | 50.0 °C@Thickness 0.800 mm | 122 °F@Thickness 0.0315 in | UL 746B |
| 85.0 °C@Thickness 1.50 mm | 185 °F@Thickness 0.0591 in | UL 746B |
| 90.0 °C@Thickness 3.00 mm | 194 °F@Thickness 0.118 in | UL 746B |
| UL RTI, Mechanical without Impact无机械冲击热指数 | 50.0 °C@Thickness 0.800 mm | 122 °F@Thickness 0.0315 in | UL 746B |
| 90.0 °C@Thickness 1.50 mm | 194 °F@Thickness 0.0591 in | UL 746B |
| 95.0 °C@Thickness 3.00 mm | 203 °F@Thickness 0.118 in | UL 746B |
| Flammability, UL94阻燃等级 | HB@Thickness 0.800 mm | HB@Thickness 0.0315 in | IEC 60695-11-10 |
| HB@Thickness 3.00 mm | HB@Thickness 0.118 in | IEC 60695-11-10 |
| Processing Properties加工性能 | Metric公制数据 | English英制数据 | Comments测试方法 |
| Melt Temperature熔体温度 | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 |
| 215 °C | 419 °F | Optimum; Injection Molding |
| 210 - 220 °C | 410 - 428 °F | Injection Molding |
| Mold Temperature模具温度 | 90.0 °C | 194 °F | optimum; Injection Molding |
| 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature干燥温度 | 80.0 °C | 176 °F | Injection Molding |
| Dry Time干燥时间 | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| Moisture Content水分含量 | <= 0.20 % | <= 0.20 % | Injection Molding |