| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.00400 - 0.00600 cm/cm@Thickness 3.20 mm | 0.00400 - 0.00600 in/in@Thickness 0.126 in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.00400 - 0.00600 cm/cm@Thickness 3.20 mm | 0.00400 - 0.00600 in/in@Thickness 0.126 in | SABIC Method |
| Melt Flow | 14.5 g/10 min@Load 2.16 kg,Temperature 260 °C | 14.5 g/10 min@Load 4.76 lb,Temperature 500 °F | ASTM D1238 |
| Spiral Flow | 68.58 cm@Temperature 260 °C | 27.00 in@Temperature 500 °F | 10 ips,3.175 X 1524 mm |
|
|
| Tensile Strength, Yield | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 50.0 % | 50.0 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 103 MPa | 14900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 2.68 GPa | 389 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 61.0 J | 45.0 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 54.0 J@Temperature -30.0 °C | 39.8 ft-lb@Temperature -22.0 °F | Instrumented Impact Energy @ peak; ASTM D3763 |
|
|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.70@Frequency 1.00e+6 Hz | 2.70@Frequency 1.00e+6 Hz | IEC 60250 |
| 2.80@Frequency 50.0 - 60.0 Hz | 2.80@Frequency 50.0 - 60.0 Hz | IEC 60250 |
| Dielectric Strength | 17.0 kV/mm@Thickness 3.20 mm | 432 kV/in@Thickness 0.126 |