| MECHANICAL 机械性能 | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 2.0 in/min | 9600 | psi | ASTM D 638 |
| Tensile Strain, brk, Type I, 2.0 in/min | 50 | % | ASTM D 638 |
| Flexural Stress, yld, 0.10 in/min, 4 in span | 14900 | psi | ASTM D 790 |
| Flexural Modulus, 0.10 in/min, 4 in span | 389000 | psi | ASTM D 790 |
| IMPACT 冲击性能 | Value | Unit | Standard |
| Izod Impact, notched, 73°F | 10 | ft-lb/in | ASTM D 256 |
| Instrumented Impact Energy @ peak, 73°F | 539 | in-lb | ASTM D 3763 |
| Instrumented Impact Energy @ peak, -22°F | 479 | in-lb | ASTM D 3763 |
| THERMAL 热性能 | Value | Unit | Standard |
| HDT, 264 psi, 0.125 in, unannealed | 190 | °F | ASTM D 648 |
| HDT, 264 psi, 0.250 in, unannealed | 195 | °F | ASTM D 648 |
| Relative Temp Index, Elec | 85 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 85 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 85 | °C | UL 746B |
| PHYSICAL物理性能 | Value | Unit | Standard |
| Specific Gravity | 1.18 | - | ASTM D 792 |
| Mold Shrinkage, flow, 0.125" (5) | 0.4 - 0.6 | % | SABIC Method |
| Mold Shrinkage, xflow, 0.125" (5) | 0.4 - 0.6 | % | SABIC Method |
| Melt Flow Rate, 260°C/2.16 kgf | 14.5 | g/10 min | ASTM D 1238 |
| Spiral Flow, 500F, 10 ips, .125 X 60 in | 27 | in | - |
| ELECTRICAL 电性能 | Value | Unit | Standard |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 |
| Hot Wire Ignition {PLC) | 2 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 3 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 0.8 mm | 35 | kV/mm | IEC 60243-1 |