pc940物性表-LEXAN 940 照明部件PC- 规格:25KG/包 

　　pc940物性表Lexan* Resin 940

　　Americas: COMMERCIAL

　　Opaque colors, medium viscosity, superior flame retardance.

　　TYPICAL PROPERTIES¹ TYPICAL VALUE Unit Standard

　　MECHANICAL

　　Tensile Stress, yld, Type I, 50 mm/min 630 kgf/cm² ASTM D 638

　　Tensile Stress, brk, Type I, 50 mm/min 560 kgf/cm² ASTM D 638

　　Tensile Strain, yld, Type I, 50 mm/min 7 % ASTM D 638

　　Tensile Strain, brk, Type I, 50 mm/min 90 % ASTM D 638

　　Flexural Stress, yld, 1.3 mm/min, 50 mm span 920 kgf/cm² ASTM D 790

　　Flexural Modulus, 1.3 mm/min, 50 mm span 22800 kgf/cm² ASTM D 790

　　Hardness, Rockwell M 70 - ASTM D 785

　　Hardness, Rockwell R 118 - ASTM D 785

　　Taber Abrasion, CS-17, 1 kg 10 mg/1000cy ASTM D 1044

　　IMPACT

　　Izod Impact, unnotched, 23°C 326 cm-kgf/cm ASTM D 4812

　　Izod Impact, notched, 23°C 65 cm-kgf/cm ASTM D 256

　　Tensile Impact, Type S 535 cm-kgf/cm² ASTM D 1822

　　Falling Dart Impact (D 3029), 23°C 1728 cm-kgf ASTM D 3029

　　THERMAL

　　Vicat Softening Temp, Rate B/50 151 °C ASTM D 1525

　　HDT, 0.45 MPa, 6.4 mm, unannealed 137 °C ASTM D 648

　　HDT, 1.82 MPa, 6.4 mm, unannealed 132 °C ASTM D 648

　　CTE, -40°C to 95°C, flow 6.84E-05 1/°C ASTM E 831

　　Thermal Conductivity 0.19 W/m-°C ASTM C 177

　　Relative Temp Index, Elec 130 °C UL 746B

　　Relative Temp Index, Mech w/impact 120 °C UL 746B

　　Relative Temp Index, Mech w/o impact 130 °C UL 746B

　　LEXAN PC沙伯基础创新塑料 940现货报价

　　低收缩韧性好高流动高透明易脱模高刚性食品级抗紫外线电气性好玻纤增强阻燃 

　　PC在汽车上的应用,预计2005年中国汽车总量达300多万辆，需求量达到3万t，因而聚碳酸酯在这一领域的应用是极有拓展潜力的。

　　PC的医疗级PC料可制作成注射器.

　　PC应用于医疗器械:由于聚碳酸酯制品可经受蒸汽、清洗剂、加热和大剂量辐射消毒，且不发生变黄和物理性能下降，因而被广泛应用于人工肾血液透析设备和其他需要在透明、直观条件下操作并需反复消毒的医疗设备中。

　　山东LEXAN PC沙伯基础创新塑料 940代理商价格