基础创新塑料总代理

　　Lexan* Resin 241R物性表

　　Americas: COMMERCIAL

　　General purpose polycarbonate with 10.5 MFR and internal mold release.

　　TYPICAL PROPERTIES¹ TYPICAL VALUE Unit Standard

　　MECHANICAL

　　Tensile Stress, yld, Type I, 50 mm/min 630 kgf/cm² ASTM D 638

　　Tensile Stress, brk, Type I, 50 mm/min 700 kgf/cm² ASTM D 638

　　Tensile Strain, yld, Type I, 50 mm/min 7 % ASTM D 638

　　Tensile Strain, brk, Type I, 50 mm/min 130 % ASTM D 638

　　Flexural Stress, yld, 1.3 mm/min, 50 mm span 980 kgf/cm² ASTM D 790

　　Flexural Modulus, 1.3 mm/min, 50 mm span 23900 kgf/cm² ASTM D 790

　　Hardness, Rockwell M 70 - ASTM D 785

　　Hardness, Rockwell R 118 - ASTM D 785

　　Taber Abrasion, CS-17, 1 kg 10 mg/1000cy ASTM D 1044

　　IMPACT

　　济南pc基础创新塑料241r价格

　　Izod Impact, unnotched, 23°C 326 cm-kgf/cm ASTM D 4812

　　Izod Impact, notched, 23°C 81 cm-kgf/cm ASTM D 256

　　Tensile Impact, Type S 589 cm-kgf/cm² ASTM D 1822

　　Falling Dart Impact (D 3029), 23°C 1728 cm-kgf ASTM D 3029

　　Instrumented Impact Energy @ peak, 23°C 650 cm-kgf ASTM D 3763

　　THERMAL

　　Vicat Softening Temp, Rate B/50 154 °C ASTM D 1525

　　HDT, 0.45 MPa, 6.4 mm, unannealed 137 °C ASTM D 648

　　HDT, 1.82 MPa, 6.4 mm, unannealed 132 °C ASTM D 648

　　CTE, -40°C to 95°C, flow 6.84E-05 1/°C ASTM E 831

　　Specific Heat 1.25 J/g-°C ASTM C 351

　　Thermal Conductivity 0.27 W/m-°C ASTM C 177

　　Relative Temp Index, Elec 130 °C UL 746B

　　台州pc基础创新塑料241r报价

　　PC聚碳酸酯材料介绍:

　　聚碳酸酯(PC)是一种无定形热塑性PC工程塑料。它具有极为优良的韧性、透明度和高的热变形温度等综合性能。在大多数应用中，一般都要求至少有上述这样性能中的两种。聚碳酸酯其他杰出的性能还有尺寸稳定性、优良的电性能和特有的耐燃性。主要应用领域为汽车、商业机器和仪表行业。聚碳酸酯年增长率约为6%。

　　PC聚碳酸酯PC的一般特性归纳如下:

　　1. 出色的物理特性

　　2. 出色的韧性

　　3. 非常好的耐热性

　　4. 抗化学作用能力一般

　　5. 透明

　　6. 中高价位

　　7. 较易加工