详细说明
物理性能编辑
| 种类的记号 | 调质记号 | 冷轧、固溶化热处理或退火状态 | 析出硬化热处理状态 | 导电% |
| 硬度HV | 屈服强度N/mm | 抗拉强度N/mm | 伸长% | 热处理记号 | 硬度HV | 屈服强度N/mm | 抗拉强度N/mm |
| 301-CSP | 1/2H | 340±30 | ≥510 | ≥930 | ≥10 | - | - | - | - | 2.3 |
| 3/4H | 400±30 | ≥745 | ≥1130 | ≥5 | - | - | - | - | 2.3 |
| H | 460±30 | ≥1030 | ≥1320 | - | - | - | - | - | 2.3 |
| EH | 510±20 | ≥1275 | ≥1570 | - | - | - | - | - | 2.3 |
| SEH | ≥530 | ≥1450 | ≥1740 | - | - | - | - | - | 2.3 |
| 304-CSP | 1/2H | 280±30 | ≥470 | ≥780 | ≥6 | - | - | - | - | 2.3 |
| 3/4H | 340±30 | ≥665 | ≥930 | ≥3 | - | - | - | - | 2.3 |
| H | ≥370 | ≥880 | ≥1130 | - | - | - | - | - | 2.3 |
| 631-CSP | 0 | ≤200 | - | ≤1030 | ≥20 | TH1050RH950 | ≥345≥392 | ≥960≥1030 | ≥1140≥1230 | 2.3 |
| 1/2H | 375±25 | - | ≥1080 | ≥5 | CH | ≥380 | ≥880 | ≥1230 | 2.3 |
| 3/4H | 425±25 | - | ≥1180 | | CH | ≥450 | ≥1080 | ≥1420 | 2.3 |
| H | ≥450 | - | ≥1420 | | CH | ≥530 | ≥1320 | ≥1720 | 2.3 |
1.屈服强度（σ0.2）:使产生永久残余塑性变形等于一定值（一般为原长度的0.2%）时的应力，称为屈服强度σ0.2。
2.抗拉强度（σb）:材料在拉伸过程中，从开始到发生断裂时所达到的最大应力值。它表示钢材抵抗断裂的能力大小。设Pb为材料被拉断前达到的最大拉力，Fo为试样截面面积，则抗拉强度σb= Pb/Fo （MPa）。
3.伸长率（δs）:材料在拉断后，其塑性伸长的长度与原试样长度的百分比叫伸长率或延伸率。
4.硬度:硬度表示材料抵抗硬物体压入其表面的能力。它是金属材料的重要性能指标之一。一般硬度越高，耐磨性越好。
化学成分编辑
品名:宝钢304不锈钢带，304不锈钢带材，304不锈钢卷带、316不锈钢卷带、301不锈钢卷带，
不锈钢带 (8张)
不锈钢材质有:SUS301(1Cr17Ni7)不锈钢卷带、SUS303（oY1Cr18Ni9）316不锈钢卷带，321不锈钢卷带，310S不锈钢卷带，不锈钢卷带，牌号:0Cr17Ni12Mo2
化学成分
C≤0.08
Si≤1.00
Mn≤2.00
P≤0.035
S≤0.03
Ni:8.0-10.0
Cr:18.0-20.0
性质编辑
拉强度(Mpa) 620 MIN
屈服强度(Mpa) 310 MIN
伸长率(%) 30 MIN
面积缩减(%) 40 MIN
304不锈钢的密度7.93 g/cm3
奥氏体不锈钢一般都用这个值
304含铬量(%) 18--20 .
304相当于我国的0Cr19Ni9 (0Cr18Ni9)不锈钢