详细说明
具有优异的耐磨性，力学性能，热力学性能高。于金属碳素钢相比，具有质量轻、加工过程简单、加工费用低、产品质量轻等优点，完全适合当前节能环保要求。
产品物性表
| 性能 Properties | 试验方法 Test Method | 单位 Unit | 典型值 Typical Value |
| 比重 Specific Gravity | ASTM D792 | | 1.39-1.49 |
| 吸水率 Water Absorption | ASTM D570 | % | 5 |
| 抗拉强度 Tensile Strength | ASTM D638 | Mpa | 190 |
| 断裂伸长率 Tensile Elongation | ASTM D638 | % | 6 |
| 弯曲强度 Flexural Strength | ASTM D790 | Mpa | 180 |
| 弯曲模量 Flexural Modulus | ASTM D790 | Mpa | 9000 |
| 悬臂梁缺口冲击强度 Izod Impact Strength | ASTM256 | J/M | 50 |
| J/M | |
| 热变形温度 Heat Deflection Temperature | ASTM D648 | ℃ | 345 |
| ℃ | |
| 阻燃等级 Flame Rating-UL | UL-94 1.5mm | | HB |
| 3.0mm | | HB |
| 体积电阻率 Volume Resistivity | ASTM D257 | Ω.cm | 1016 |
| 耐电弧性能 Arc resistance | GB1411-78 | /s | 140 |