油墨专用料PMMA CM-211

　　油墨专用料PMMA CM-211性能项目 试验条件[状态] 测试方法 测试数据  数据单位 

　　基本性能  假密度  ---  ASTM D-1182  0.77  gm/cm3  

　　吸水率  ---  ASTM D-570  0.3  %  

　　油墨专用料PMMA CM-211物理性能  

　　成型收缩率  ---  ASTM D-955  0.002-0.006  mm/mm  

　　比重  ---  ASTM D-792  1.19  ---  

　　流动系数  ---  ASTM D-1238  16  gm/10min  

　　油墨专用料PMMA CM-211机械性能  

　　硬度  ---  ASTM D-785  M-84  ---  

　　全光透过率  ---  ASTM D-1003  92  %  

　　引张强度  ---  ASTM D-638/PSI  9200/650  Kg/cm2  

　　弯曲强度  ---  ASTM D-790/PSI  13200/930  Kg/cm2  

　　延伸率  ---  ASTM D-638  5.0  %  

　　抗冲击力  ---  ASTM D-256  0.37  ft-lbs/in2  

　　抗冲击力  ---  ASTM D-256  2.0  kg-cm/cm  

　　油墨专用料PMMA CM-211电气性能  

　　曲折率  ---  ASTM D-542  1.491  ---  

　　绝缘耐力  ---  ASTM D-149  500  Volts/Mil  

　　诱电率  ---  ASTM D-150-647b  3.7  ---  

　　诱电率力  ---  ASTM D-150-647  0.5  ---  

　　失电率  ---  ASTM D-150  0.19  ---  

　　体积固有抵抗  ---  ASTM D-257  1015  Ω.m  

　　油墨专用料PMMA CM-211热 性 能  

　　燃烧率  ---  ---  1/16  UL-94  

　　热变形温度  ---  ASTM D-648  90/194  °C/°F  

　　维卡软化点  ---  ASTM D-1525  102/216  °C/°F  

　　台湾奇美PMMA产品加工条件 :

　　压克力粒的加工一般为注射成型亦可押出或压缩成型，成型温度约在170~240°C，其特别注意如下:

　　(1)吸湿性特高:加工成型前预备干燥是必需的，预备干燥温度需低于树脂粒软化点10~15°C，干燥时间4~6hrs加工前水份射出≦0.05%，押出≦0.02%。

　　(2)成型加工温度注意不可过高。

　　(3)互混性:高温料(CM-205)不可以与中低温料混合(CM-207 & CM-211)。

　　二次加工因表面光滑亦无法电镀，但能涂装真空蒸著(烫金)及印刷，产品溶接时可氯化甲烷，亦可使用超音波熔接。

　　预热干燥温度介于85~90°C

　　模温为50~70°C

　　射出缸温介于210~250°C

　　射出压力为800~1400psi / 70~90kg/cm2

　　※以上资料仅供参考用，实际加工条件将依射出机之型式、模头之构造以成型之特性而调整